Equivalent Material of 316Ti Stainless Steel  Sheet

Standard Specification Of 316Ti Plate

316Ti stainless steel composition content.

YS (MPa) ≥205
TS (MPa) ≥520
EL (%) ≥40
Hv around 200 °
Thickness: cold 2B board (0.09-6.0mm);
Hot rolled industrial plate No.1(3-50mm) medium thick plate, chemical plate, high temperature plate;
Width: 5mm-- 850mm steel belt;
1000, 1219, 1250, 1500, 1800, 2000mm coil, flat plate
Surface: 2B smooth surface, No.1 industrial surface, BA (6K) mirror, 8K mirror, 9K mirror, drawing surface, frosted surface.
Origin: domestic, imported (Sweden, Japan, Finland, South Korea, South Africa, Taiwan)

316Ti Stainless steel sheet manufacturer

SUS316Ti stainless steel is austenitic stainless steel, SUS316Ti stainless steel is added to SUS316 steel to improve the intergranular corrosion resistance.
Sus316Ti stainless steel has strong intergranular corrosion resistance. It is widely used in petrochemical industry, mechanical and electrical hardware, shipbuilding and power plant.

316Ti Stainless steel sheet Price in China ,Manufacturer of 316Ti Stainless Steel sheet

316Ti stainless steel plate national standard 0Cr18Ni12Mo2Ti Chinese brand is 1Cr18Ni12Mo2Ti stainless steel plate, 316Ti stainless steel plate is added in SUS316 steel Ti to improve the intergranular corrosion resistance.
Used to resist sulfuric acid, phosphoric acid, acetic acid, acetic acid equipment.

These attributes refer to products in similar, but not identical, attributes that are specified for other products, such as plates and forgings in their respective specifications.
Lower minimum pre and post thermal temperatures reduce the incidence of welds, cracking and simplify welding.
Low hardness decreases in the heat affected zone to minimize deterioration in the mold performance.

316Ti Characteristic machining technology

1D -- The surface has discontinuous granular shape, also known as fog surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2D - A slightly silvery white colour.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling.
2B -- Silver white with better gloss and flatness than a 2D surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + quenching and tempering rolling.
Ba - Excellent surface gloss, high reflectivity, like a mirror surface.
Processing technology: hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + surface polishing + quenching and tempering rolling.
No.3 -- Good gloss, coarse grain surface.
Processing technology: polishing and tempering rolling for 2D or 2B with 100~120 abrasive materials (JIS R6002).
No.4 -- Good gloss, fine lines on the surface.
Processing process: polishing and tempering rolling for 2D or 2B with 150~180 abrasive materials (JIS R6002).
HL -- Silver grey with hair streaks.
Processing technology: 2D products or 2B products with appropriate granularity of abrasive materials for polishing the surface is a continuous abrasive grain.
MIRRO -- Specular.
Processing technology: 2D products or 2B products with appropriate granularity of the grinding material grinding and polishing to the mirror effect.